A Comparison of Mechanical Properties and Hydrogen Embrittlement Resistance of Austempered vs Quenched and Tempered 4340
- PDF / 109,270 Bytes
- 1 Pages / 593.972 x 792 pts Page_size
- 95 Downloads / 241 Views
DOI: 10.1007/s11661-008-9521-6 Ó The Minerals, Metals & Materials Society and ASM International 2008
Erratum to: METALLURGICAL AND MATERIALS TRANSACTIONS A, Vol. 39A, No. 3, March 2008 DOI 10.1007/s11661-007-9451-8
THE footnotes for Table III were inadvertently omitted from the original article: Approximate UTS values:[24] *Austempered: 1580 MPa (229 ksi). **Q&T: 1450 MPa (210 ksi). Also, in the caption for Figure 3, the Mo content should have read 0.32 percent Mo, as opposed to 0.23 percent Mo.
JOHN M. TARTAGLIA, Engineering Manager and Senior Metallurgical Engineer, and KRISTEN A. LAZZARI and GRACE P. HUI, Engineering Associates, are with Stork Climax Research Services, Wixom, MI 48393. Contact e-mail: john.tartaglia@ stork.com. KATHY L. HAYRYNEN, Technical Director, is with the Technologies Division, Applied Process, Inc., Livonia 48150, MI. The online version of the original article can be found under doi: 10.1007/s11661-007-9451-8. Article published online March 18, 2008 1236—VOLUME 39A, MAY 2008