Calorimetric evaluation of nonequilibrium state in as-melt spun Al-1.72 and Al-3.12 At. Pct Cu Alloys and Al-6.74, Al-8.
- PDF / 287,196 Bytes
- 3 Pages / 598.28 x 778.28 pts Page_size
- 69 Downloads / 121 Views
The authors would like to acknowledge the financial support of Alcoa, Anglo Blackwells Ltd., and the Science and Engineering Research Council. They are also grateful to D.A. Granger (Alcoa Technical Center) and S.R. Thistlethwaite (formerly with Anglo Blackwells) for many useful discussions regarding this work.
REFERENCES 1. R. Mehrabian, M. Keane, and M.C. Flemings: Metall. Trans., 1970, vol. 1, pp. 1209-20. 2. A.L. Maples and D.R. Poirier: Metall. Trans. B, 1984, vol. 15B, pp. 163-72. 3. K.S. Yeum and D.R. Poirier: Cast Met., 1988, vol. l, pp. 161-70. 4. M.C. Flemings and G.E. Nereo: Trans. TMS-A1ME, 1967, vol. 239, pp. 1449-61. 5. M.C. Flemings, R. Mehrabian, and G.E. Nereo: Trans. TMSAIME, 1968, vol. 242, pp. 41-49. 6. S.H. Davis: J. Fluid Mech., 1990, vol. 212, pp. 241-62. 7. S.C. Flood and J.D. Hunt: in Metals Handbook, 9th ed. ASM INTERNATIONAL, Metals Park, OH, 1988, vol. 15, pp. 130-36. 8. D.A. Granger: in Treatise on Materials Science and Technology, R.D. Doherty and A.K. Vasudevan, eds., Academic Press, London, 1989, vol. 31, pp. 109-34. 9. H. Yu and D.A. Granger: in Aluminum Alloys Their Physical and Mechanical Properties, EMAS, London, 1986, vol. 1, pp. 17-28; also in Fundamentals of Alloy Solidification Applied to Industrial Processes, NASA Conf. Pub. 2337, NASA, Cleveland, OH, 1984, pp. 157-68. 10. M.G. Chu and J.E. Jacoby: in Light Metals 1990, C.M. Bickert, ed., TMS, Warrendale, PA, 1990, pp. 925-30. 11. D.G. McCartney: Int. Mater. Rev., 1989, vol. 34, pp. 247-60. 12. S.M. Ahmady, D.G. McCartney, and S.R. Thistlethwaite: in Light Metals 1990, C.M. Bickert, ed., TMS, Warrendale, PA, 1990, pp. 837-43. 13. G.S. Cole: in Solidification, ASM, Metals Park, OH, 1971, pp. 201-74. 14. H. Fredriksson and M. Hitlert: J. Mater. Sci., 1971, vol. 6, pp. 1350-54. 15. H. Kato and J.R. Cahoon: Metall. Trans. A, 1985, vol. 16A, pp. 690-93. 16. D.G. McCartney, J.D. Hunt, and R.M. Jordan: Metall. Trans. A, 1980, vol. l l A , pp. 1243-49. 17. P. Desnain, Y. Fautrelle, J.L. Meyer, J.P. Riquet, and F. Durand: Acta Metall. Mater., 1990, voi. 38, pp. 1513-23. 18. L.F. Mondolfo: in Aluminum Alloys: Structures and Properties, Butterworth and Co. Ltd. London, 1976. 19. J.D. Hunt: Mater. Sci. Eng., 1984, vol. 65, pp. 75-84. 20. L.A. Tarshis, J.L. Walker, and J.W. Rutter: Metall. Trans., 1971, vol. 2, pp. 2589-97. 21. T. Abel Engh: Principles of Metal Refining, Oxford University Press, New York, NY, 1992, p. 349. 22. D.R. Poirier: Metall. Trans. B, 1987, vol. 18B, pp. 245-55. 23. K. Kubota, K. Murakami, and T. Okamoto: Mater. Sci. Eng., 1986, vol. 79, pp. 67-77. 1102--VOLUME 25A, MAY 1994
Calorimetric Evaluation of Nonequilibrium State in As-Melt Spun A1-1.72 and AI-3.12 At. Pct Cu Alloys and AI-6.74, AI-8.48, and AI-11.97 At. Pct Si Alloys Y. ZHANG, T. YAMANE, S. SAJI, and J. TAKAHASHI Rapid solidification produces a nonequilibrium state in an alloy system, so that an enthalpy difference, ~[./ne exists between as-melt spun ribbon and the fully annealed ribbon at room temperature. In previous w o r k s , t1'2'31 w e have prop
Data Loading...