Effects of sample geometry on deformation modes of bulk metallic glasses at the nano/micrometer scale

  • PDF / 658,853 Bytes
  • 4 Pages / 584.957 x 782.986 pts Page_size
  • 55 Downloads / 201 Views

DOWNLOAD

REPORT


Peter K. Liaw The Department of Materials Science and Engineering, The University of Tennessee, Knoxville, Tennessee 37996-2200 (Received 16 July 2009; accepted 31 August 2009)

Intense debates have been prompted concerning whether homogeneous deformation can be achieved in bulk metallic glasses at room temperature through the suppression of shear bands at the submicron scale. In this short communication, we demonstrate that multiple shear banding can be successfully attained via a proper modification of the microsample geometry, resulting in the appearance of a homogeneous deformation mode at the submicron scale. However, the apparent deformation homogeneity in our microcompression experiment is a manifestation of the sample geometry effect on the propagation rather than nucleation of shear bands.

Understanding the behavior of shear bands in bulk metallic glasses (BMGs) is critical in the design of a new class of BMGs with superior mechanical properties. In BMG bulk samples, shear bands tend to propagate in a catastrophic way, resulting in the subsequent brittlelike fracture, which renders the BMGs with limited ductility at room temperature.1 However, at the micrometer scale, shear bands were found to behave in a ductile manner, propagating without causing the sudden fracture of the microsample throughout a large plastic deformation process.2 Moreover, it was reported that shear bands could even be completely suppressed by reducing the sample size into the submicron scale, which led to a homogeneous deformation mode at room temperature.3,4 However, the idea of the shear-band suppression is controversial and was later challenged by a few researchers based on their results of the microcompression experiments,5–7 in which no homogeneous deformation mode was observed on the micropillars even though their diameters were reduced to a level less than that observed in the homogeneous deformation mode. It can be argued that the difference of the experimental results originates from the chemical composition of the microsamples, i.e., different BMGs have different critical length scales below which the shear bands cannot be nucleated. Thus, the homogeneous deformation is still an intrinsic effect, reflecting the shear-banding behavior at the small size scale. However, there is another extrinsic effect that could a)

Address all correspondence to this author. e-mail: [email protected] DOI: 10.1557/JMR.2009.0414 J. Mater. Res., Vol. 24, No. 11, Nov 2009

http://journals.cambridge.org

Downloaded: 16 Mar 2015

also cause the apparent deformation homogeneity, but was somehow ignored in previous studies,2–4,6 which is derived from the sample geometry and the associated boundary conditions. In mechanical testing of single crystals, it is known that the grips play an important role in determining the deformation morphology of a tensile specimen. If the lateral translations of both grips are constrained, a dislocation single slip is not favored, and, thus, the resulting deformation morphology is a reflection of the combined effect

Data Loading...