ABSTRACT Stacking faults at order interfaces in TiAI have been examined by HREM. In addition to very extensive OCISF formation, C-core dislocation complexes spread over two parallel { 1111 planes have been observed at order interfaces lying predominantly parallel to the original (0002), planes. Such C-cores, corresponding to 1/2

Recommend Documents

The Correlation of Slip between Adjacent Lamellae in TiAl.

153 70 4MB

Quasi-Seeding Mechanism in Lamellae Alignment of TiAl Alloys During Directional Solidification

136 52 4MB

Caudal Lamellae

137 88 115KB

Educational Interfaces Between Mathematics and Industry at School Level

191 78 6MB

Dislocation Core Spreading at Interfaces between Crystalline and Amorphous Solids

277 42 1MB

Interdiffusion Between Mo and TiAl

166 49 411KB

Thermal Stability of Structurally Controlled Lamellae and Hexagonal Mesoporous Silicate Thin Films

143 48 342KB

Proteins at Titanium Interfaces

199 85 4MB

Pattern Formation at Interfaces

261 63 7MB

Water at functional interfaces

202 43 331KB

Accelerated sintering of SiC Nanopowder with Stacking Disorder-Order Transformation

148 84 418KB

Soft Matter at Aqueous Interfaces

208 46 15MB