Hot hardness has been measured in seven isostmctural Be 12 X compounds: Be12Cr, Bei2 Mn, Be^V, Be 12 Mo, Be12Ti, Be12Ta, and Be 12 Nb. All vacuum-hot-pressed (VHP) materials exhibited similar hardness levels (800 to 1000 kg/mm 2 ) at low temperatures (

Recommend Documents

Deformation Mechanisms in Be 12 X Compounds

250 26 2MB

Electron affinities of X 12 O 12 (X = Be, Mg, and Ca), X 12 N 12 (X = B, Al, and Ga), and X 12 P 12 (X = B, Al, and Ga)

189 96 769KB

Applications of Intermetallic Compounds

271 108 5MB

Miscellaneous Applications of Intermetallic Compounds

274 5 658KB

Electromagnetic Applications of Intermetallic Compounds

279 10 3MB

Fundamental Properties of Intermetallic Compounds

240 31 1MB

X-puzzel #12

181 80 100KB

Fabrication of cellular NiTi intermetallic compounds

200 25 296KB

High-Temperature Applications of Intermetallic Compounds

219 59 2MB

Mechanism of Diffusion in Intermetallic Compounds

228 37 353KB

Deformation Twinning in Ordered Intermetallic Compounds

262 96 475KB

Formation of Intermetallic Compounds During Explosive Welding

233 91 7MB