Lattice thermal vibration and its nonharmonic effect in Nd-doped rare-earth vanadates
- PDF / 500,004 Bytes
- 6 Pages / 612 x 792 pts (letter) Page_size
- 80 Downloads / 202 Views
X.L. Meng, X.F. Cheng, L.J. Qin, L. Zhu, and Z.H. Yang Institute of Crystal Materials, and National Laboratory of Crystal Materials, Shandong University, Jinan 250100, China (Received 19 February 2004; accepted 12 July 2004)
The 0.5 at.% Nd-doped gadolinium and yttrium orthovanadate, Nd:GdVO4 (NGV) and Nd:YVO4 (NYV), crystallize in the tetragonal space group I41/amd and are of a zircon-type structure with the lattice constants a ⳱ b ⳱ 0.7212(6) and c ⳱ 0.6348(3) nm for NGV and a ⳱ b ⳱ 0.7123(5) and c ⳱ 0.6292(5) nm for NYV. At high and room temperatures, the Raman spectra of NYV are much the same; however, the Raman spectra of NGV are different from those of NYV. The scattering intensity of NGV is largely stronger than that of NYV. Nonharmonic effect of the lattice thermal vibrations, including the thermal conductivity and expansion, is theoretically and experimentally discussed. The theoretical results roughly indicate that a crystal with the larger integrated intensities of the Raman-scattering peaks under the cutoff value of linear dependence of Debye frequency versus the temperature has the larger thermal conductivity. The experimental data of the thermal conductivity of the five samples show that the thermal conductivity of NGV is more outstanding than that of NYV in every direction. Compared the integrated intensity ratio IG/IY between the NGV and NYV Raman-scattering peaks under the cutoff wavenumber of Debye frequency with the ratio G/Y of their crystal thermal conductivity, it may be seen that the Raman results are basically in agreement with the conductivity measurements within our experimental error. The experimental datum of the thermal conductivity of NYAG (Nd-doped yttrium aluminum garnet) with the cubic symmetry and stable laser properties and thermodynamics parameters, which is often considered as a comparable standard, approximately approaches to the average value of the NGV thermal conductivity in the a and c directions. The thermal-expansion data of NGV exhibit its small line-expansion coefficients, which imply that the large thermal conductivity is needed and existential and that NGV is more capable to bear a large temperature gradient, therefore, is also more suitable as a solid-state laser material than NYV crystals.
I. INTRODUCTION
All rare-earth (RE) vanadates and their solid solutions crystallize in the tetragonal space group I41/amd (D19 4h) and are excellent as host materials for the miniature lasers. The activated RE ions are suitable in the strong tetragonal crystal field with the site symmetry D2d, which lacks inversion symmetry and thereby increases the probability of the parity-forbidden f→f transitions.1,2 In a)
Address all correspondence to this author. e-mail: [email protected] DOI: 10.1557/JMR.2005.0013 30
http://journals.cambridge.org
J. Mater. Res., Vol. 20, No. 1, Jan 2005 Downloaded: 28 Mar 2015
recent years, the laser crystals pumped by a laser diode (LD) have attracted attention due to their excellent laser properties, for example, having compact structure, being fu
Data Loading...