Localized Multi-axis Loading Impact on Interconnect Thermal Cycling Performance in Via-in-Pad Plated Over (VIPPO) Board
- PDF / 5,404,196 Bytes
- 11 Pages / 593.972 x 792 pts Page_size
- 99 Downloads / 214 Views
https://doi.org/10.1007/s11664-020-08409-y Ó 2020 The Minerals, Metals & Materials Society
TMS2020 MICROELECTRONIC PACKAGING, INTERCONNECT, AND PB-FREE SOLDER
Localized Multi-axis Loading Impact on Interconnect Thermal Cycling Performance in Via-in-Pad Plated Over (VIPPO) Board Configuration MOHAMED SHEIKH,1 ANDY HSIAO,1 WEIDONG XIE,2 STEVEN PERNG,2 and TAE-KYU LEE 1,3 1.—Portland State University, Portland, OR, USA. 2.—Cisco Systems, San Jose, CA, USA. 3.—e-mail: [email protected]
The effects of different via pad configurations on solder joint reliability during thermal cycling have been investigated. Implementation of the via-in-pad plated over (VIPPO) design configuration induced additional loading conditions for each ball grid array interconnection, resulting in a lower than expected thermal cycling performance. Thermal cycling of memory components with 0.8-mm pitch and 300-lm-diameter solder joints with and without VIPPO configuration boards have been evaluated. It was identified that specific pad design parameters degraded the thermal cycling performance. Under thermal cycling, Printed circuit boards with all-VIPPO pads and all-dog-bone pads were found to have a higher thermal cycling performance than the unevenly distributed mixed VIPPO/dog-bone pad configuration. The characteristic life for the mixed VIPPO configuration shows a performance level of 56% compared to the all-dog-bone configuration and 44% compared to the all-VIPPO configuration. Electron backscattered diffraction images revealed straining within the solder joints stemming from tension and compression due to different via pad configurations. The laser profilometer height measurement showed that dog-bone pads have larger z-axis movement than VIPPO pads, inducing localized tension within the solder joints. The heating and cooling behavior observed for VIPPO and dog-bone via pads during thermal cycling induced localized tension and compression that exacerbated joint failure and accelerated their degradation. The temperature behavior of the different pads under thermal cycling suggests that thermal cycling is a complex multi-axis phenomenon. Key words: Via-in-pad plated over (VIPPO), multi-axis loading, thermal cycling, interconnection, BGA
INTRODUCTION As miniaturization continues to drive the evolution of electronic components, recent industry trends have placed more emphasis on component functionality as well as design for reliability. For
(Received June 11, 2020; accepted August 11, 2020)
memory packages with a multi-stacked die configuration, design for reliability principles pushes the industry to consider reliability issues previously overlooked. This pushing is most likely to increase with their various design configurations not limited to just the package but also including the attached board, a common combination for high-performance applications such as servers and routers.1–4 Either solder mask-defined or non-solder mask-defined copper pad components are traditionally connected