Microscopic Examination of the Interface Region in 6061-AI/SIC Composites Reinforced with As-Received and Oxidized SiC Particles H. RIBES, M. SUltRY, G. L'ESPI~RANCE, and J.G. LEGOUX Aluminum (6061) matrix composites reinforced with different SiC particles were processed. Black SiC particles were used in their as-received form or after artificial oxidation, leading to a 50-nm-thick SiO2 layer surrounding the SiC particles. The manufacturing route used was the compocasting technique, which allows maintenance of the semisolid slurry at relatively low temperatures (

Recommend Documents

Modification of the interface in SiC/Al composites

198 68 1MB

Interface Reaction in SiC Reinforced Al 3 Ti-Based Intermetallic Matrix Composites

172 27 4MB

Interface characterization of duplex metal-coated SiC fiber-reinforced Ti-15-3 matrix composites

201 74 8MB

Oxidized starch films reinforced with natural halloysite

196 12 605KB

Interface control and design for SiC fiber-reinforced titanium aluminide composites

187 59 2MB

Fiber and interface fracture in singlecrystal aluminum/SiC fiber composites

206 3 2MB

Bonding Mechanism and Interface Enhancement of Bamboo Fiber Reinforced Composites

187 21 11MB

Significance of Interface Design Aspects and Characteristics in Cu/SiC p Composites Fabricated by the Powder Metallurgy

190 57 4MB

SiC whisker- and C fiber-reinforced calcium phosphate composites

201 17 1MB

Effect of SiC p volume fraction on the microstructure and tensile properties of SiC p /2024 Al-based composites prepared

276 86 2MB

Role of interface properties on the toughness of brittle matrix composites reinforced with ductile fibers

172 17 905KB

Interface characterization of fiber-reinforced Ni 3 Al matrix composites

208 65 5MB