Superconducting Parent Compound Pr 2 CuO 4 Achieved by Special Post-Reduction
- PDF / 233,826 Bytes
- 6 Pages / 432 x 648 pts Page_size
- 33 Downloads / 140 Views
Superconducting Parent Compound Pr2CuO4 Achieved by Special Post-Reduction Hideki Yamamoto1, Osamu Matsumoto2, Keitaro Yamagami1, Michio Naito2, and Yoshiharu Krockenberger1 1 NTT Basic Research Laboratories., NTT Corporation, Atsugi-shi, Kanagawa, 243-0198, Japan 2 Department of Applied Physics, Tokyo University of Agriculture and Technology, Koganei-shi, Tokyo, 184-8588, Japan ABSTRACT It is commonly believed that the parent compounds of high-Tc cupratres are, universally, charge transfer insulators and triggered by Mott physics. In our experiments using metal-organic decomposition (MOD), however, accumulating evidences show that the parent compounds of “electron-doped” superconductors, RE2-xCexCuO4 [RE = rare earth ion] with x = 0, are not Mott insulators but superconductors [1-5]. They have a Tc of 30 K and crystallize in the Nd2CuO4 (T’) structure. Most likely, the sharp contradiction between our results and commonly achieved data originates from the complicated oxygen chemistry in these materials. The as-synthesized specimens contain a fair amount of impurity interstitial oxygen. Throughout the reduction process it is required to remove exclusively impurity oxygen while preserving regular oxygen site occupied in order to obtain superconductivity. With decreasing x the constraints of the reduction process are getting more tight. In this study, we systematically investigated the postannealing process using MBE-grown T’-Pr2CuO4 films. The MBE films were reduced ex-situ in a tubular furnace following a specially designed 2-step process, as in the case of MOD films. The films were annealed at Ta = 700 - 850°C in a reducing atmosphere (PO2 = 2 x 10-5 - 2 x 10-3 atm) and finally reduced at a lower temperature Tred = 450 – 700°C under vacuum (< 10-4 Torr). The film properties systematically changed with Ta, PO2, and Tred. The optimized Tred varies from 475°C to 650°C mainly depending on Ta, since the microstructure and grain size of the films are determined by Ta. Optimal superconducting properties are Tc of 26 K, while ρ(300 K) = 250 μΩcm, and RRR ~ 10. We believe the combination of thin-film synthesis and specially designed post-reduction process enabled us to obtain nearly intact CuO2 planes. Samples prepared by above-mentioned method unveiled the intrinsic properties of the parent compounds, which are not triggered by Mott physics. This result also agrees with the recent calculation result indicating the parent compounds with T’ structure are not charge transfer insulators [6-8]. INTRODUCTION Recently, grain boundary/size engineering is getting a more and more popular concept in the field of solid state ionics [9], where research on ionic conduction itself is essential to improve the performance of, e.g., batteries. Here, we show such an approach gives an important clue to understand still puzzling electronic properties and the electronic phase diagram of high-Tc cuprate superconductors. Cuprate superconductors are the record holder in Tc [10]. The electronic phase diagram of the cuprates, however, remains enigmat
Data Loading...