Erratum: "Effects of boron on the deformation behavior of N13AI" [J. Mater. Res. 9, 1742-1754 (1994)] J. A. Brusso and D. E. Mikkola Department of Metallurgical and Materials Engineering, Michigan Technological University, Houghton, Michigan 49931 (Received 12 January 1995; accepted 13 January 1995)
After this article was published in the July issue of Journal of Materials Research, the authors discovered a few errors. On p. 1746 (last column), Baker et al. were misquoted as suggesting "that some of the boron occupies tetrahedral sites . . . ". The word "tetrahedral" in this sentence should be replaced by "edge octahedral". A similar substitution must be made in the first column of p. 1747. The sentence should read, "For this situation, boron seems less likely to occupy the higher energy edge octahedral sites." Also in the first column of p. 1747, the
1062
J. Mater. Res., Vol. 10, No. 4, Apr 1995
word "center" should be added so that the next sentence reads "In support of this, Masahashi et al. . . . suggested that boron occupies the center octahedral sites." There is one final correction that needs to be made. Reference 46 should be as follows: 46. H.G. Bohn, J.M. Williams, J.H. Barrett, and C. T. Liu, in High-Temperature Ordered Intermetallic Alloys II, edited by N.S. Stoloff, C.C. Koch, C.T. Liu, and O. Izumi (Mater. Res. Soc. Symp. Proc. 81, Pittsburgh, PA, 1987), p. 127.
1995 Materials Research Society
Data Loading...