Internal displacement reactions in multicomponent oxides. Part I. Line compounds with narrow homogeneity range
- PDF / 564,295 Bytes
- 10 Pages / 612 x 792 pts (letter) Page_size
- 53 Downloads / 185 Views
N
A displacement reaction between a metal and an oxide involves the reduction of a noble oxide by a reactive metal. Previous studies of solid-state displacement reactions between metals and oxides[1–6] have identified several types of reaction morphologies and their relationship to the thermodynamic and diffusional transport properties of product phases. Some of the reaction couples considered were Cu2O/Co,[1] Cu2O/Ni,[1] Cu2O/Fe,[1,2] Cu2O/Co1xFex,[3] NiO/Fe,[1,4] NiO/Al,[5] and NiO/Mg.[6] In particular, Rapp et al.[1] have considered the reactive interface stability as a function of the diffusional rate control in the product phases. Internal reactions occur inside a metal or ceramic matrix; an example is the well-known internal oxidation of alloys.[7] Schmalzried[8,9] has considered internal oxidation and reduction reactions in multicomponent oxides and an extensive review is given by Schmalzried and Backhaus-Ricoult.[10] Shook et al.[11] have considered the internal displacement reaction in a metal matrix by studying the reaction between Cr and MoO2 inside a Ni matrix. As part of a study of the internal displacement reactions in multicomponent oxides, the reaction between a metal and ternary oxide compound of a narrow homogeneity range (a line compound) is considered in this article, along with the results for a model reaction between Fe and NiTiO3 at 1273 K. Reactions involving solid solutions of oxide compounds will be considered in Part II of this series of articles.[12] These reactions can
S.N.S. REDDY, Senior Engineer and L.B. WIGGINS, Senior Technical Staff Member, are with the Systems and Technology Group, IBM Corporation, Hopewell Junction, NY 12533. Contact e-mail: [email protected] D.N. LEONARD, Graduate Student, is with the Department of Materials Science, North Carolina State University, Raleigh, NC 27695. K.T. JACOB, Professor, is with the Department of Metallurgy, Indian Institute of Science, Bangalore5600 12, India. Manuscript submitted July 13, 2004. METALLURGICAL AND MATERIALS TRANSACTIONS A
be exploited to manufacture metal-ceramic composites having unique physical and mechanical properties. II. DISPLACEMENT REACTIONS INSIDE A LINE COMPOUND An internal displacement reaction in an oxide compound of a narrow homogeneity range is defined by the following chemical reaction: A (metal) BCOmn (oxide) “B”(metal) “ACOmn” (oxide); G1 0 [1] where G1 is the Gibbs energy change for the reaction. In Reaction [1], cation B is displaced by cation A in the oxide, without changing the crystal structure of the oxide, and cation C does not participate in the chemical exchange reaction. During the reaction, “B” is typically precipitated as A-B alloy and the product oxide, “ACOmn”, is usually (A,B)COmn. The reaction is associated with a volume increase in the product zone, mainly due to the volume of “B” precipitate. The oxide systems in which Reaction [1] is possible are illustrated in Figure 1 and discussed in the following. Consider three binary oxides, AOm, BOm, and COn; AOm and BOm have the sa
Data Loading...