Drainage of high-consistency fiber-laden aqueous foams
- PDF / 2,138,895 Bytes
- 16 Pages / 547.087 x 737.008 pts Page_size
- 50 Downloads / 209 Views
(0123456789().,-volV) ( 01234567 89().,-volV)
ORIGINAL RESEARCH
Drainage of high-consistency fiber-laden aqueous foams Antti I. Koponen
. Oleg Timofeev . Ari Ja¨sberg . Harri Kiiskinen
Received: 14 April 2020 / Accepted: 22 August 2020 Ó The Author(s) 2020
Abstract Lightweight lignocellulosic fibrous materials (LLFMs) offer a sustainable and biodegradable alternative in many applications. Enthusiastic interest in these materials has recently grown together with the newly risen interest in foam forming. Foam bubbles restrain fiber flocculation, and foam formed structures have high uniformity. Moreover, the bubbles support the fibrous structure during manufacturing enabling the formation of highly porous structures. Mechanical pressure cannot be applied in the manufacture of LLFMs as the materials would lose their porous structure. Water is therefore typically removed by a combination of drainage and thermal drying. Thermal drying of porous materials has been studied intensively. However, there are only a few studies on the drainage of fiber-laden foams. Thus, in this work, we conducted a systematic analysis of this topic. Our findings show that after drainage a stationary vertical moisture profile similar to that of pure foams is developed. Raising the initial fiber consistency was found to increase the final fiber consistency of the foam until the drainage ceased. Increasing mold height was found to increase the final consistency considerably. Without vacuum and heating, the shrinkage of samples during drainage was only slightly higher than
A. I. Koponen (&) O. Timofeev A. Ja¨sberg H. Kiiskinen VTT Technical Research Centre of Finland, P.O. Box 1603, 40101 Jyva¨skyla¨, Finland e-mail: [email protected]
the volume of the drained water. Drainage rate and final consistency increased clearly with increasing vacuum, but simultaneously sample shrinkage increased considerably. The best compromise was obtained with a vacuum of 0.5 kPa, which increased the final consistency by 60% without extra shrinkage. Using warm foam and heating the foam during drainage increased the final consistency considerably, but this also led to significant shrinkage of the sample. Keywords Fiber-laden foam Foam forming Drying Drainage Lightweight cellulose materials Lightweight fibrous structures
Introduction Lightweight lignocellulosic fibrous materials (LLFMs) offer a sustainable and biodegradable alternative in many applications such as thermal insulation (Po¨hler et al. 2017), sound insulation (Nechita and Na˘stac 2018; Debeleac et al. 2019), interior decoration (Ha¨rka¨salmi et al. 2017; Siljander et al. 2019), polymer-impregnated composites, and packaging (Satyanarayana et al. 2009; Huber et al. 2012). As lignocellulosic fibers have strong aggregation tendency, LLFMs are difficult to produce with conventional water forming. However, due to the recent
123
Cellulose
resurgence of foam forming, interest in these materials is now growing rapidly. In foam forming, fibers are mixed with water and surfactants to cre