The Cracking of Sol-Gel Films During Drying
- PDF / 1,341,734 Bytes
- 6 Pages / 420.48 x 639 pts Page_size
- 3 Downloads / 208 Views
THE CRACKING OF SOL-GEL FILMS DURING DRYING
TERRY J. GARINO Sandia National Laboratories, Albuquerque, NM 87185
Electronic
Ceramics
Division
1842,
ABSTRACT
The cracking behavior of acidic silica sol-gel films during drying and low temperature heat treatment was studied. Films that cracked during drying exhibited a variety of unusual crack morphologies including sinusoidal cracks and parallel crack pairs. The effects of the water content of the sol and temperature on the critical thickness above which cracking of the films occurred were determined. The critical thickness decreased with increasing water content, most likely because the surface tension of the liquid in the pores of the gel increases with water content and because sols with low water concentrations did not gel until the solvent had evaporated. To determine why the critical thickness decreased with temperature, thermal analysis and shrinkage measurements of both constrained and unconstrained films were performed. Thermogravimetric analysis indicated that rapid weight loss occurred in the temperature region where the rapid decrease in critical thickness occurred. A small amount of shrinkage of the films also occurred in this region. Finally, shrinkage measurements of films debonded from the substrate indicated that shrinkage was very anisotropic with nearly all of the shrinkage occurring in the plane of'the film and very little in the thickness direction.
INTRODUCTION
One limitation of the sol-gel process for forming films is that cracking of the films can occur during drying or heating. For a given sol, a critical film thickness exists above which cracking occurs. The critical thickness is generally
Data Loading...