Polymer Patterning via Electrohydrodynamic Instabilities Katie Copenhaver, Marianna Luna, Jason Nadler Georgia Tech Research Institute, Atlanta, GA 30318, United States of America

ABSTRACT

Electrohydrodynamic (EHD) instabilities can be induced in polymers by placing a polymer film above its Tg in a strong electric field between two capacitor plates or electrodes. The polymer experiences an electrostatic stress at the interface between the polymer and air due to a mismatch in their dielectric constants. This stress, along with thermal fluctuations, induces small magnitude capillary waves in the polymer film, and the minima and maxima of those waves experience slightly different electric field strengths. In a sufficiently strong electric field, the capillary wave maxima, where the distances between the polymer film and the top electrode(s) are the smallest, are eventually drawn up to the top electrode. The wavelength of the instabilities in the film and the ability of the polymer to be drawn upward is a dependent on the competition between surface tension forces and the electrostatic stress imparted on the polymer. While EHD instabilities are typically used to pattern polymer surfaces on a nanometer-scale, instabilities have been induced in polymer films with air gaps up to 500 μm. Upper electrodes with non-planar structures have also been used to induce instabilities in polymer films, resulting in patterned polymer surfaces without contact. Size, shape, arrangement, and placement of the upper electrode relative to the polymer film and lower electrode, as well as the processing conditions such as temperature and applied voltage, can all be modified to produce a desired array of structures with tailored performance characteristics. Patterned polymer surfaces can provide high-index contrast over a periodic matrix with 3-dimensional element shapes. The dielectric contrast and array pitch and height can be tuned to control specular reflection and achieve specific scattering characteristics. Surfaces with tailored scattering characteristics in the aforementioned ranges could be useful in producing frequency-selective windows for glare reduction, anti-reflective solar cells with enhanced efficiency, surface waveguides and whispering gallery-mode resonator arrays for integrated photonics and sensors, and surfaces with controlled emissivity for directed heat dissipation.

Downloaded from https://www.cambridge.org/core. University of Cincinnati Libraries, on 11 Feb 2019 at 17:52:48, subject to the Cambridge Core terms of use, available at https://www.cambridge.org/core/terms. https://doi.org/10.1557/adv.2019.63

INTRODUCTION Much research in metamaterial and photonic bandgap structures is focused on the challenges of fabricating uniform and ordered structure arrays over large areas at a micro- and nano-scale. Electrohydrodynamic (EHD) instabilities have been induced in polymer films as a means of producing a structured array on these length scales. Wh