Effect of individual phase properties and volume fractions on the strain partitioning, deformation localization and tens
- PDF / 3,613,908 Bytes
- 13 Pages / 595.276 x 790.866 pts Page_size
- 9 Downloads / 220 Views
Sådhanå (2020)45:235 https://doi.org/10.1007/s12046-020-01438-7
Sadhana(0123456789().,-volV)FT3](012345 6789().,-volV)
Effect of individual phase properties and volume fractions on the strain partitioning, deformation localization and tensile properties of DP steels AMIT KUMAR RANA1,*, SURAJIT KUMAR PAUL2 and PARTHA PRATIM DEY1 1
Department of Mechanical Engineering, Indian Institute of Engineering Science and Technology, Shibpur, Howrah 711103, India 2 Department of Mechanical Engineering, Indian Institute of Technology Patna, Patna, Bihar 801106, India e-mail: [email protected]; [email protected]; [email protected] MS received 6 February 2020; revised 24 May 2020; accepted 1 July 2020 Abstract. Deformation band localization modes, uniform tensile strength, and uniform elongation of FerriteMartensite Dual-Phase (DP) steels are analyzed by finite element (FE) study. Treating the microstructure inhomogeneity as the sole cause of imperfection, failure initiation is predicted as the natural fallout of plastic instability caused by load drop because of localized plastic strain in the Representative Volume Element (RVE) during straining. Strain partitioning between two phases (ferrite matrix and martensite island) are investigated on RVEs, and it reveals that the increase of martensite yield stress decreases the plastic deformation and increases the stress state in martensite. Whereas, a decrease in martensite island volume fraction (Vm) results in the reduction of plastic deformation and stress state in the island. Studies are then carried out to investigate the effects of the ferrite-martensite flow properties and martensite volume fraction on the macroscopic tensile deformation behavior and band localization of DP steels. Micromechanical based FE simulation results emphasize that an increase in initial yield strength and volume fraction of martensite increases the ultimate tensile stress (UTS) with the decrease in uniform elongation. Similarly, as the hardening rate of ferrite increases, it increases the ultimate tensile stress (UTS) and uniform elongation. Additionally, deformation band localization modes alter from inclined to perpendicular to the loading axis with an increase in martensite volume fraction and initial yield strength of martensite. The knowledge of this work can be used to design DP steels with desired mechanical properties. Keywords.
Strain partitioning; deformation localization; dual phase steel; micromechanical model.
1. Introduction Dual phase (DP) steels are low (or medium) carbon microalloyed steels, characterized by a ferritic multiphase structure in which martensite islands are dispersed on the ferrite matrix. Ferrite-Martensite DP steel shows the demanding automotive material characteristics in which the ferrite phase ensures good formability, whereas the hard second phase of martensite island is the strengthening constituent. Maintaining the suitable proportions of the two phases (matrix and island) allow low yielding stress, high elongation, and well-being flow stress curve w