Biological Response of Intramedullary Bone to Poly-L-Lactic Acid
- PDF / 310,465 Bytes
- 5 Pages / 420.48 x 639 pts Page_size
- 92 Downloads / 207 Views
Biological Response of Intramedullary Bone to Poly-L-Lactic Acid J. Suganuma,M.D. H. Alexander, Ph.D. J. Traub, B.S. J. L. Ricci, Ph.D. Department of Bioengineering Hospital for Joint Diseases Orthopaedic Institute 301 East 17th Street New York NY
Abstract Bioabsorbable synthetic polymers have been studied for their possible application in absorbable internal fracture fixation devices. The current study examines the biological response of intramedullary bone to PLLA (poly-L-lactic acid). PLLA degrades at a rate sufficiently slow to be useful for fracture fixation and undergoes hydrolytic deesterification to form metabolites normally found in the body. Nevertheless, the lactic-acid-rich degradation products have the potential to significantly lower the local pH in a closed space surrounded by bone. It is hypothesized that this acidity may tend to cause abnormal bone resorption and/or demineralization. PLLA (Medisorb, Du Pont), with a molecular weight of 1.0 x 105 daltons, was chosen for this study. PLLA coupons were made by heating the polymer pellets to 180 0 C and pressing them. Ultrahigh-molecular-weight polyethylene chambers with ingrowth channels running widthwise, were lined with coupons of the test material and with stainless steel (SS) and implanted in the femurs of eight skeletally mature hound dogs. Two dogs each were killed 3, 6, 12, and 24 weeks postoperatively. From an associated in vitro study,the molecular weight of the PLLA was found to decrease with immersion time to 0.92, 0.85, and 0.69 of original molecular weights by 6, 12, and 24 weeks, respectively. Ingrown bone was seen between both PLLA and SS coupons, and no resorption areas existed between bone and the chambers at 3 and 6 weeks. By 12 weeks, no bone was found ingrown in the PLLA chambers. Indeed, femoral bone around the chamber had resorbed. By contrast, the amount of bone grown into the SS chambers increased and the femoral bone was in contact with the chamber. The affinity of in-
tramedullary bone to PLLA was greater than that of SS at the early time periods. No inflammatory cells were seen. This may explain earlier claims of osteogenic potential. Once the degradation of PLLA had started (as reflected by the molecular weight data), the affinity of PLLA to bone reduced drastically. Not only the bone ingrowth between the PLLA coupons but also the bone surrounding the chamber was resorbed. This resorption of bone is probably caused by the influence of the degradation products of PLLA that increase osteoclastic activity. The degradation rate accelerated between 6 and 12 weeks. Mat. Res. Soc. Symp. Proc. Vol. 252. 'c1992 Materials Research Society
340
Though the resorption of bone around the chamber was not massive in this study, it might jeopardize bone union if it were used for internal fixation of a bone fracture. These findings are significant in that experimental oa-polyester-based fracture fixation systems are currently in development and clinical trials in the United States, Europe, and Japan.